Синтез керамических материалов из смеси Hf-Ti-C-N-B
In this work, the structure and phase composition of the ceramic material obtained as a result of combustion of the Hf-Ti-C-B powder mixture in nitrogen are investigated. The initial components of the charge were taken in the mass ratio: 35Ti + 5C + 25Hf + 5B. The nitrogen pressure during synthesis...
| Published in: | Перспективы развития фундаментальных наук. Т. 2 : сборник научных трудов XIX Международной конференции студентов, аспирантов и молодых ученых, 26-29 апреля 2022 г. Т. 2 : Химия. С. 85-87 |
|---|---|
| Main Author: | |
| Other Authors: | , |
| Format: | Book Chapter |
| Language: | Russian |
| Subjects: | |
| Online Access: | http://vital.lib.tsu.ru/vital/access/manager/Repository/koha:001006540 |
| Summary: | In this work, the structure and phase composition of the ceramic material obtained as a result of combustion of the Hf-Ti-C-B powder mixture in nitrogen are investigated. The initial components of the charge were taken in the mass ratio: 35Ti + 5C + 25Hf + 5B. The nitrogen pressure during synthesis was 3.5 MPa. It is established that the synthesis products contain two phases: HfTiCN and TiB2. The analysis of the content of phases in the synthesis products by the Rietveld method showed that the proportion of TiB2 is ~ 60 wt.%, and HfTiCN ~ 40 wt. %. |
|---|---|
| Bibliography: | Библиогр.: 3 назв. |
| ISBN: | 9785438710837 9785438710813 |