Multilayer antireflection optical coatings based on Nb, Si and Al oxides for nonlinear ZnGeP2 crystals
The effect of the designed antireflection coatings based on Nb2O5/Al2O3 and Nb2O5/SiO2 pairs of materials on the laser-induced damage threshold (LIDT) of ZnGeP2 crystals at a wavelength of 2097 nm is shown. The coating was applied using the ion-beam sputtering (IBS) method. The LIDT of the sample co...
| Published in: | Proceedings of SPIE Vol. 12341 : 28th International Symposium on Atmospheric and Ocean Optics: Atmospheric Physics, 2022, Tomsk, Russia. P. 123413E-1-123413E-4 |
|---|---|
| Other Authors: | , , , |
| Format: | Article |
| Language: | English |
| Subjects: | |
| Online Access: | http://vital.lib.tsu.ru/vital/access/manager/Repository/koha:001009262 Перейти в каталог НБ ТГУ |
| Summary: | The effect of the designed antireflection coatings based on Nb2O5/Al2O3 and Nb2O5/SiO2 pairs of materials on the laser-induced damage threshold (LIDT) of ZnGeP2 crystals at a wavelength of 2097 nm is shown. The coating was applied using the ion-beam sputtering (IBS) method. The LIDT of the sample coated with Nb2O5/SiO2 was W0d = 1.8 J/cm2. The LIDT of a sample coated with Nb2O5/Al2O3 is W0d = 2.35 J/cm2. The presence of silicon conglomerates in the antireflection coating leads to a decrease the LIDT of a nonlinear crystal due to local thermomechanical stresses and scattering of the incident laser radiation. |
|---|---|