Влияние режима термической обработки на закономерности мартенситных превращений в монокристаллах сплава Ni48Fe19Ga27Co6
The influence of thermal treatment regime on mechanism of thermoelastic martensite transformations has been studied in [001]L21-oriented single crystals of Ni48Fe19Ga27Co6 ferromagnetic alloy. The investigation was carried out in as-grown state and after high-temperature annealing at 1373 K, 0,5 h a...
| Published in: | Перспективы развития фундаментальных наук. Т. 1 : сборник научных трудов XX Международной конференции студентов, аспирантов и молодых ученых, 25-28 апреля 2023 г. Т. 1 : Физика. С. 225-227 |
|---|---|
| Main Author: | |
| Other Authors: | |
| Format: | Book Chapter |
| Language: | Russian |
| Subjects: | |
| Online Access: | http://vital.lib.tsu.ru/vital/access/manager/Repository/koha:001147012 Перейти в каталог НБ ТГУ |
| LEADER | 02684naa a2200337 c 4500 | ||
|---|---|---|---|
| 001 | koha001147012 | ||
| 005 | 20241105165617.0 | ||
| 007 | cr | | ||
| 008 | 241031s2023 ru fs 100 0 rus d | ||
| 035 | |a koha001147012 | ||
| 040 | |a RU-ToGU |b rus |c RU-ToGU | ||
| 100 | 1 | |a Курлевская, Ирина Дмитриевна |9 760672 | |
| 245 | 1 | 0 | |a Влияние режима термической обработки на закономерности мартенситных превращений в монокристаллах сплава Ni48Fe19Ga27Co6 |c И. Д. Курлевская, А. Б. Тохметова |
| 246 | 1 | 1 | |a The influence of thermal treatment regime on mechanism of martensite transformations in single crystals of Ni48Fe19Ga27Co6 alloy |
| 336 | |a Текст | ||
| 337 | |a электронный | ||
| 504 | |a Библиогр.: 2 назв. | ||
| 520 | 3 | |a The influence of thermal treatment regime on mechanism of thermoelastic martensite transformations has been studied in [001]L21-oriented single crystals of Ni48Fe19Ga27Co6 ferromagnetic alloy. The investigation was carried out in as-grown state and after high-temperature annealing at 1373 K, 0,5 h and at 1448 K, 1 h, where heterophase structure with γ(γ')-particles is formed. It was shown, that γ(γ')-particles became larger, martensitic transformation temperatures, thermal and mechanical hysteresis increased with higher temperature and time treatment in comparison with the initial as-grown state. The maximum elastocaloric effect reaches ~9 K in as-grown state and after annealing at 1373 K, 0,5 h. | |
| 653 | |a термическая обработка | ||
| 653 | |a мартенситные превращения | ||
| 653 | |a ферромагнитные сплавы | ||
| 653 | |a экспериментальные исследования | ||
| 655 | 4 | |a статьи в сборниках |9 976053 | |
| 700 | 1 | |a Тохметова, Аида Бауыржановна |9 457878 | |
| 773 | 0 | |t Перспективы развития фундаментальных наук. Т. 1 : сборник научных трудов XX Международной конференции студентов, аспирантов и молодых ученых, 25-28 апреля 2023 г. |d Томск, 2023 |g Т. 1 : Физика. С. 225-227 |z 9785438711377 |z 9785438711360 | |
| 852 | 4 | |a RU-ToGU | |
| 856 | 4 | |u http://vital.lib.tsu.ru/vital/access/manager/Repository/koha:001147012 | |
| 856 | |y Перейти в каталог НБ ТГУ |u https://koha.lib.tsu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=1147012 | ||
| 908 | |a статья | ||
| 999 | |c 1147012 |d 1147012 | ||
| 039 | |b 100 | ||