Влияние микроструктуры и фазового состава на механические свойства композита ZrO2-MgO с бимодальной поровой структурой
In this paper porous ceramics based on the Zr02-Mg0 system were studied. It was shown, that the addition of an organic pore-forming particles make it possible to obtain a bimodal pore structure. X-ray diffraction analysis showed that with the increasing of MgO concentration, the average size of Zr02...
| Published in: | Перспективы развития фундаментальных наук. Т. 1 : сборник научных трудов XV Международной конференции студентов, аспирантов и молодых ученых, 24-27 апреля 2018 г. Т. 1 : Физика. С. 78-80 |
|---|---|
| Main Author: | |
| Other Authors: | , |
| Format: | Book Chapter |
| Language: | Russian |
| Subjects: | |
| Online Access: | http://vital.lib.tsu.ru/vital/access/manager/Repository/vtls:000636360 Перейти в каталог НБ ТГУ |
| LEADER | 02806naa a2200385 c 4500 | ||
|---|---|---|---|
| 001 | vtls000636360 | ||
| 003 | RU-ToGU | ||
| 005 | 20240216115241.0 | ||
| 007 | cr | | ||
| 008 | 181114s2018 ru fs 100 0 rus d | ||
| 035 | |a to000636360 | ||
| 039 | 9 | |a 201811141353 |b 100 |c 201811141233 |d VLOAD |y 201811141225 |z Александр Эльверович Гилязов | |
| 040 | |a RU-ToGU |b rus |c RU-ToGU | ||
| 100 | 1 | |a Буяков, Алесь Сергеевич |9 143732 | |
| 245 | 1 | 0 | |a Влияние микроструктуры и фазового состава на механические свойства композита ZrO2-MgO с бимодальной поровой структурой |c А. С. Буяков, Е. О. Васильева, Д. А. Ткачев |
| 246 | 1 | 1 | |a Effect of microstructure and phase composition on mechanical properties of the composite ZrO2-MgO with a bimodal pore structure |
| 504 | |a Библиогр.: 5 назв. | ||
| 520 | 3 | |a In this paper porous ceramics based on the Zr02-Mg0 system were studied. It was shown, that the addition of an organic pore-forming particles make it possible to obtain a bimodal pore structure. X-ray diffraction analysis showed that with the increasing of MgO concentration, the average size of Zr02 and MgO crystallites grows up and their crystal lattice microdistortion decrease. Strength with increasing of MgO concentration is increasing and the dependence of compressive strength from microstresses was found. | |
| 653 | |a оксид магния | ||
| 653 | |a диоксид циркония | ||
| 653 | |a спекание | ||
| 653 | |a рентгеноструктурный анализ | ||
| 653 | |a пределы прочности | ||
| 653 | |a керамика | ||
| 653 | |a экспериментальные данные | ||
| 653 | |a пористые керамические материалы | ||
| 655 | 4 | |a статьи в сборниках |9 879352 | |
| 700 | 1 | |a Васильева, Елизавета Олеговна |9 375980 | |
| 700 | 1 | |a Ткачев, Дмитрий Александрович |9 481610 | |
| 773 | 0 | |t Перспективы развития фундаментальных наук. Т. 1 : сборник научных трудов XV Международной конференции студентов, аспирантов и молодых ученых, 24-27 апреля 2018 г. |d Томск, 2018 |g Т. 1 : Физика. С. 78-80 |z 9785946217248 |z 9785946217231 |w to000633022 | |
| 852 | 4 | |a RU-ToGU | |
| 856 | 7 | |u http://vital.lib.tsu.ru/vital/access/manager/Repository/vtls:000636360 | |
| 856 | |y Перейти в каталог НБ ТГУ |u https://koha.lib.tsu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=442851 | ||
| 908 | |a статья | ||
| 999 | |c 442851 |d 442851 | ||