Особенности деформированной микроструктуры ферритно-мартенситной стали ЭП-823 после высокотемпературной термомеханической обработки
The features of the microstructure of 12%o chromium ferritic-martensitic steel EP-823 near the neck region of samples deformed by tension at T=-70--40 °C, T = 20 °C and in the temperature range close to the operating temperatures of a nuclear reactor T = 650-720 °C after high - temperature thermomec...
| Published in: | Перспективы развития фундаментальных наук. Т. 1 : сборник научных трудов XVIII Международной конференции студентов, аспирантов и молодых ученых, 27-30 апреля 2021 г. Т. 1 : Физика. С. 46-48 |
|---|---|
| Main Author: | |
| Format: | Book Chapter |
| Language: | Russian |
| Subjects: | |
| Online Access: | http://vital.lib.tsu.ru/vital/access/manager/Repository/koha:000846271 Перейти в каталог НБ ТГУ |
| LEADER | 02661naa a2200325 c 4500 | ||
|---|---|---|---|
| 001 | koha000846271 | ||
| 005 | 20230503134425.0 | ||
| 007 | cr | | ||
| 008 | 220209s2021 ru fs 100 0 rus d | ||
| 035 | |a koha000846271 | ||
| 040 | |a RU-ToGU |b rus |c RU-ToGU | ||
| 100 | 1 | |a Алмаева, Ксения Викторовна |9 252903 | |
| 245 | 1 | 0 | |a Особенности деформированной микроструктуры ферритно-мартенситной стали ЭП-823 после высокотемпературной термомеханической обработки |c К. В. Алмаева |
| 246 | 1 | 1 | |a Features of the deformed microstructure of ferritic-martensitic steel EP-823 after high-temperature thermomechanical treatment |
| 336 | |a Текст | ||
| 337 | |a электронный | ||
| 504 | |a Библиогр.: 3 назв. | ||
| 520 | 3 | |a The features of the microstructure of 12%o chromium ferritic-martensitic steel EP-823 near the neck region of samples deformed by tension at T=-70--40 °C, T = 20 °C and in the temperature range close to the operating temperatures of a nuclear reactor T = 650-720 °C after high - temperature thermomechanical treatment (HTMT) are investigated. It is shown that at T=-70 °C, -40 °C and 20 °C plastic deformation leads to curvature and fragmentation of martensitic lamellae and formation of new low-angle boundaries. Deformation near the operating temperature range contributes to the development of dynamic polygonization, recrystallization and an increase in the density and sizes of carbide particles. | |
| 653 | |a ферритно-мартенситные стали | ||
| 653 | |a высокотемпературная термомеханическая обработка | ||
| 653 | |a пластическая деформация | ||
| 653 | |a механические свойства сталей | ||
| 655 | 4 | |a статьи в сборниках |9 879352 | |
| 773 | 0 | |t Перспективы развития фундаментальных наук. Т. 1 : сборник научных трудов XVIII Международной конференции студентов, аспирантов и молодых ученых, 27-30 апреля 2021 г. |d Томск, 2021 |g Т. 1 : Физика. С. 46-48 |z 9785438710110 |z 9785438710103 | |
| 852 | 4 | |a RU-ToGU | |
| 856 | 4 | |u http://vital.lib.tsu.ru/vital/access/manager/Repository/koha:000846271 | |
| 856 | |y Перейти в каталог НБ ТГУ |u https://koha.lib.tsu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=846271 | ||
| 908 | |a статья | ||
| 999 | |c 846271 |d 846271 | ||
| 039 | |b 100 | ||