Laser preparation of bimetallic Au-Pt nanoparticles for modification of dark TiO2 photocatalyst
Bimetallic Au-Pt nanoparticles with different molar ratios were obtained using laser synthesis (Nd:YAG laser with the parameters: 1064 nm, 180 mJ, 7 ns, and 20 Hz). The bimetallic nature of the particles was confirmed by X-ray diffraction and UV-visible spectroscopy. According to the transmission el...
| Published in: | Bulletin of the Russian Academy of Sciences: Physics Vol. 88, suppl. № 2. P. S154-S159 |
|---|---|
| Other Authors: | , , , |
| Format: | Article |
| Language: | English |
| Subjects: | |
| Online Access: | https://vital.lib.tsu.ru/vital/access/manager/Repository/koha:001159549 Перейти в каталог НБ ТГУ |
| LEADER | 02623nab a2200349 c 4500 | ||
|---|---|---|---|
| 001 | koha001159549 | ||
| 005 | 20250627171712.0 | ||
| 007 | cr | | ||
| 008 | 250625|2024 ru s a eng d | ||
| 024 | 7 | |a 10.1134/S1062873824708948 |2 doi | |
| 035 | |a koha001159549 | ||
| 040 | |a RU-ToGU |b rus |c RU-ToGU | ||
| 245 | 1 | 0 | |a Laser preparation of bimetallic Au-Pt nanoparticles for modification of dark TiO2 photocatalyst |c E. D. Fakhrutdinova, M. A. Krainyukova, A. V. Volokitina, V. A. Svetlichnyi |
| 336 | |a Текст | ||
| 337 | |a электронный | ||
| 504 | |a Библиогр.: 30 назв. | ||
| 520 | 3 | |a Bimetallic Au-Pt nanoparticles with different molar ratios were obtained using laser synthesis (Nd:YAG laser with the parameters: 1064 nm, 180 mJ, 7 ns, and 20 Hz). The bimetallic nature of the particles was confirmed by X-ray diffraction and UV-visible spectroscopy. According to the transmission electron microscopy data, it was found that the bimetallic nanoparticles were represented by the alloy particles of an elongated shape with a diameter of 5-10 nm. Then, the bimetallic particles were decorated with a powder of highly defective dark titania by impregnation.The photocatalytic activity of the TiO₂ with deposited bimetallic particles was estimated in the reactions of Rhodamine B dye decomposition and hydrogen production under LED irradiation with a wavelength of 375 nm. It was found that the highest photocatalytic activity in the series was exhibited by the samples with the deposited bimetallic particles, where the Au : Pt ratios was 50 : 50 and 30 : 70. It was also shown that the TiO₂ nanoparticles decorated with the bimetallic Au : Pt NPs exhibited higher activity compared to the samples successively modified with monometals in the same ratios. | |
| 653 | |a биметаллические наночастицы | ||
| 653 | |a импульсная лазерная абляция | ||
| 653 | |a фотокатализ | ||
| 655 | 4 | |a статьи в журналах | |
| 700 | 1 | |a Fakhrutdinova, Elena D. |9 567766 | |
| 700 | 1 | |a Krainyukova, M. A |9 980644 | |
| 700 | 1 | |a Volokitina, A. V. |9 798732 | |
| 700 | 1 | |a Svetlichnyi, Valerii A. |9 562988 | |
| 773 | 0 | |t Bulletin of the Russian Academy of Sciences: Physics |d 2024 |g Vol. 88, suppl. № 2. P. S154-S159 |x 1062-8738 | |
| 852 | 4 | |a RU-ToGU | |
| 856 | 4 | |u https://vital.lib.tsu.ru/vital/access/manager/Repository/koha:001159549 | |
| 856 | |y Перейти в каталог НБ ТГУ |u https://koha.lib.tsu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=1159549 | ||
| 908 | |a статья | ||
| 039 | |b 100 | ||
| 999 | |c 1159549 |d 1159549 | ||